การวิเคราะห์การผสมกันของพอลิแอลแล็ฑไทด์และพอลิดีแล็ฑไทด๔ด้วยวิธีการหล่อฟิล์ม (Thai)
In: Journal of Science & Technology MSU, Jg. 38 (2019-09-01), Heft 5, S. 534-538
academicJournal
Zugriff:
Polylactide is the most widely used biodegradable polymer. The high thermal stability and mechanical properties of polylactide makes permit a wide range of industrial applications. Polylactide has two isomers; Poly (L-lactide) (PLLA) and Poly (D-lactide) (PDLA). Blended PLLA and PDLA forms in a stereocomplex have melting points around 220230°C higher than pure PLLA or PDLA 50°C. เท this experiment, PLLA and PDLA were blended by a solution casting process using dichloromethane as solvent. The ratios of PLLA:PDLA were 100:0, 90:10, 70:30, 50:50, 30:70, 10:90 and 0:100. The blended films were then tested for their mechanical properties and thermal stability. The results showed that PLLA:PDLA at 50:50 had only one melting point around 225°c while the melting temperatures of neat PLLA and PDLA were about 172-175°c. Moreover, the blend materials also had higher tensile strength than pure PLLA or PDLA 55% as well as higher thermal stability than pure PLLA or PDLA. [ABSTRACT FROM AUTHOR]
Copyright of Journal of Science & Technology MSU is the property of Mahasarakham University and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)
Titel: |
การวิเคราะห์การผสมกันของพอลิแอลแล็ฑไทด์และพอลิดีแล็ฑไทด๔ด้วยวิธีการหล่อฟิล์ม (Thai)
|
---|---|
Autor/in / Beteiligte Person: | อัคคะประส, ทิพย์ธิดา ; ศรีเทพ, ยศฐา |
Zeitschrift: | Journal of Science & Technology MSU, Jg. 38 (2019-09-01), Heft 5, S. 534-538 |